Oxygen Reduction on Platinum-Nickel and Platinum-Cobalt Alloy Based Catalysts for High Temperature Proton Exchange Membrane Fuel Cells

Catalyst layers, with commercial PtNi/TKK (TECNiE52; platinum 46.5 wt%), PtCo/TKK (TEC36E52; platinum 45.8 wt%) catalysts, and an in-house catalyst PtNi-NC (platinum 38.4 wt%), synthesised using acoustic mixer and a tube furnace, are prepared using three different ionomers: 20 wt% Nafion®, 60 wt% polytetrafluoroethylene (PTFE), and an in-house 5 wt% ionomer (‘Ionomer X’). These inks are bar-coated onto carbon paper gas diffusion layers (GDLs), which are cut into 3 cm × 5 cm pieces. The coated layers are tested for oxygen reduction in a commercial gas diffusion electrode (GDE) test cell, FlexCell® (Gaskatel GmbH, Germany), using 85 wt% phosphoric acid at both room temperature and at 155°C. This study evaluates the polynorbornene (PNB)-based in-house ionomer performance as binder and in-house catalyst oxygen reduction reaction (ORR) activity in comparison to commercial products. The catalyst layers are characterised using X-ray diffraction (XRD) analysis, X-ray photoelectron spectroscopy (XPS), and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). Among the catalyst layers prepared with PTFE ionomer and tested at 155°C, the in-house catalyst demonstrates the highest ORR activity. Ionomer X proves to be a good candidate to be used as a per- and polyfluoroalkyl-free binder for high-temperature (HT) proton exchange membrane fuel cell (PEMFC) applications.. Authors: Linge, Jonas [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0009000739702666); Lyu, Xiang [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000208673248); Yu, Haoran [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000173042840); Meyer III, Harry [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000349941664); Lehmann, Michelle [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)]. DOE Contract: AC05-00OR22725. Subjects: 85 wt% phosphoric acid; high temperature gas diffusion electrodes; ionomers; oxygen reduction reaction